Filler Wire TIG / MIG Stainless Steel Manufacturers, Suppliers And Exporter
Filler Wire TIG / MIG Stainless Steel : Extra low carbon stainless steel filler wire suitable for welding Stainless Steel grades, the low carbon content reduces the possibility of inter granular corrosion. This filler wire is primarily used for welding low carbon molybdenum bearing austenitic alloys.
Filler Wire TIG / MIG Stainless Steel Manufacturers, Suppliers And Exporter at Ahmedabad, Bangalore, Chennai, Mumbai, Surat, Vadodara, Gujarat And all over India.
| Grade | Size (mm) |
Typical All weld Deposit Analysis(%) | Typical All Weld Mechanical Properties | Applications | ||||||||
| C | Si | Mn | Cr | Ni | Mo | Y.P. N/mm2 (Ksi) |
T.S. N/mm2 (Ksi) |
EI. (%) |
I.V. oC,J (oF,Ft-LBs.) |
|||
| ER308/308H | 0.05 | 0.46 | 1.65 | 20.45 | 9.85 | – | – | 570 (83) |
41 | – | For unstabalized stainless steels such as type 301,302,304,304H, 305, 308 & 308H | |
| ER-308L | 2.4 3.2 4.0 4.8 |
0.03 | 0.48 | 1.67 | 19.22 | 9.77 | – | – | 570 (83) |
41 | – | For low carbon of 18% Cr -8% Ni stainless steel. |
| ER308LSi | 0.019 | 0.85 | 1.65 | 20.65 | 10.00 | 570 (83) |
41 | – | It is used to weld base metal of similar composition such as AISI 301, 302, 304, 304L, 305, 308, 308L & 347 | |||
| ER-309L | 2.4 3.2 4.0 4.8 |
0.03 | 0.47 | 1.47 | 23.50 | 13.41 | – | – | 570 (83) |
40 | – | For low carbon of 22% Cr- 12% Ni stainless steel.and dissimilar steels welding. |
| ER-309LSi | 0.019 | 0.84 | 1.85 | 23.50 | 12.95 | – | 570 (83) |
40 | With higher silicon content to improve the bead appearance mostly used for welding dissimilar materials like mild steel to stainless steel, for a barrier layer in stainless overlays. | |||
| ER-309LMo | 0.014 | 0.50 | 1.75 | 24.10 | 12.9 | 2.40 | Used for joining unalloyed/lowalloy steels/ cast steel grades or stainless steels/ heat-resistance chromium steels/ cast steel grades to austenitic steels/ cast steel grades as well as for overlay cladding. | |||||
| ER-310 | 0.10 | 0.47 | 1.82 | 26.50 | 21.08 | – | 420 (61) |
580 (84) |
37 | – | For welding type AIS 1 310, 304 clad stainless steel. | |
| ER-316L | 2.4 3.2 4.0 4.8 |
0.03 | 0.46 | 1.73 | 19.20 | 12.50 | 2.47 | – | 550 (80) |
41 | – | For low carbon of 18% Cr-8% Ni – 2.5% Mo stainless steel. |
| ER-316Lsi | 0.022 | 0.85 | 1.80 | 19.25 | 12.6 | 2.45 | – | 550 (80) |
41 | – | For low carbon of 18% Cr-8% Ni – 2.5% Mo stainless steel with higher silicon content | |
| ER-317/ ER-317L |
0.02 | 0.40 | 1.72 | 19.10 | 13.54 | Mo 3.50 |
410 (59) |
570 (83) |
39 | – | For welding similar stainless steels.Offers higher resistance to pitting and crevice corrosion. | |
| ER-318 | 0.045 | 0.52 | 1.86 | 18.95 | 11.75 | 2.45 | Use for welding of Base Metal Grade of 316Ti | |||||
| ER-320 | 0.02 | 0.27 | 0.46 | 19.73 | 33.48 | Mo 2.12 cb&Ta 0.40 Cu3.20 |
460 (67) |
610 (88) |
41 | – | For welding similar metals in wrought and cast forms. good corrosion resistance to a wide range of chemical environments. | |
| ER-347 ER-347L |
0.03 | 0.41 | 1.68 | 20.22 | 9.87 | Cb&Ta 0.88 |
450 (65) |
616 (89) |
39 | – | For welding 321 and 347. Niobium stabilized reduce chance of chromium carbide precipitation and consequent intergranular corrosion. | |
| ER-410 | 0.06 | 0.41 | 0.53 | 12.93 | 0.42 | Mo | 850oC*2 hr. | – | For welding types 403, 410, and 416. Also used as overlay on carbon steels to resist corrosion, erosion or acbrasion. | |||
| 310 (45) |
530 (77) |
35 | ||||||||||
| ER-410 NiMo |
0.03 | 0.41 | 0.54 | 12.15 | 4.12 | Mo 0.62 |
850oC*2 hr. | as weld HRC 37-40 |
For welding cast and wrought material of similar chemical composition. | |||
| 850 (123) |
950 (138) |
17 | ||||||||||
| ER-430 | 0.06 | 0.38 | 0.55 | 16.79 | 0.45 | Mo 0.16 |
850oC*2 hr. | – | For welding similar alloys, overlay and thermal spraying. Good ductility in head-treated condition. | |||
| ER-383 | 0.02 | 0.22 | 2.63 | 29.2 | 36.4 | Mo 4.35 Nb 1.83 |
350 (51) |
550 (80) |
30 | – | For welding 825,alloy 28 and alloy 20.Corrosion resistance characteristics. | |
| ER-385 | 0.02 | 0.35 | 1.71 | 20.2 | 25.60 | Mo 4.52 Cu 1.5 |
410 (59) |
610 (88) |
35 | -196o, 130 (-321o, 96) |
For welding similar metals and for fabrication of equipment handling sulfuric acid and chloride containing media. | |
| ER-312 | 0.12 | 0.50 | 1.48 | 29.85 | 9.05 | – | 620 (90) |
770 (112) |
27 | – | For welding dissimilar steels, high strength and high yield steels. | |