Stellite Rods

COBALT ALLOY-1 Composition :

Co : Ni : Fe : Al : B : C : Cr :
Bal. max,3 max,2.5 2.45 31
Mn : Mo : P : S : Si : Ti : W :
1 1 13
It is resistant to oxidizing and reducing atmospheres up to 2100 deg F. It has excellent strength at elevated temperatures that is maintained through aging characteristics occurring in the temperature range of 1300 deg F to 2100 deg F. Hardness : 53 Rockwell “C”
COBALT ALLOY-6 Composition :

Co : Ni : Fe : Al : B : C : Cr :
Bal. max,3 max.3 1.2 28
Mn : Mo : P : S : Si : Ti : W :
1 1.1 4.5
It is the most generally useful cobalt alloy, having excellent resistance to many forms of mechanical and chemical degradation over a wide temperature range. Particular attributes are its outstanding self-material, high temperature hardness and high resistance to cavitations erosion. The alloy is ideally suited to a variety of hard facing processes. Hardness : 47 Rockwell “C”
COBALT ALLOY-12 Composition :

Co : Ni : Fe : Al : B : C : Cr :
Bal. max,3 max,2.5 1.4-1.85 29.5
Mn : Mo : P : S : Si : Ti : W :
1 1.5 8.5
It is cobalt-base alloy having high heat and corrosion resistance with excellent wear and abrasion resistance. It is a machinable hard facing alloy used for facing the cutting edges of long knives in the carpet, plastics, paper and chemical industries. Hardness : 47 Rockwell “C”
COBALT ALLOY-21 Composition :

Co : Ni : Fe : Al : B : C : Cr :
Bal. max,3 max,2.5 0.25 27
Mn : Mo : P : S : Si : Ti : W :
1 5.5 1.5
It is resistant to oxidizing and reducing atmospheres up to 2100 deg F. It has excellent strength at elevated temperatures that is maintained through aging characteristics occurring in the temperature range of 1300 deg F to 2100 deg F. Hardness : 36 Rockwell “C”