Filler Wire Tig / Mig Stainless Steel
Grade Size
(mm)
Typical All weld Deposit Analysis(%) Typical All Weld Mechanical Properties Applications
C Si Mn Cr Ni Mo Y.P.
N/mm2
(Ksi)
T.S.
N/mm2
(Ksi)
EI.
(%)
I.V.
oC,J
(oF,Ft-LBs.)
ER308/308H 0.05 0.46 1.65 20.45 9.85 - - 570
(83)
41      - For unstabalized stainless steels such as type 301,302,304,304H, 305, 308 & 308H
ER-308L 2.4
3.2
4.0
4.8
0.03 0.48 1.67 19.22 9.77 - - 570
(83)
41 - For low carbon of 18% Cr -8% Ni stainless steel.
ER308LSi 0.019 0.85 1.65 20.65 10.00 570
(83)
41 - It is used to weld base metal of similar composition such as AISI 301, 302, 304, 304L, 305, 308, 308L & 347
ER-309L 2.4
3.2
4.0
4.8
0.03 0.47 1.47 23.50 13.41 - - 570
(83)
40 - For low carbon of 22% Cr- 12% Ni stainless steel.and dissimilar steels welding.
ER-309LSi 0.019 0.84 1.85 23.50 12.95 - 570
(83)
40 With higher silicon content to improve the bead appearance mostly used for welding dissimilar materials like mild steel to stainless steel, for a barrier layer in stainless overlays.
ER-309LMo 0.014 0.50 1.75 24.10 12.9 2.40 Used for joining unalloyed/lowalloy steels/ cast steel grades or stainless steels/ heat-resistance chromium steels/ cast steel grades to austenitic steels/ cast steel grades as well as for overlay cladding.
ER-310 0.10 0.47 1.82 26.50 21.08 - 420
(61)
580
(84)
37 - For welding type AIS 1 310, 304 clad stainless steel.
ER-316L 2.4
3.2
4.0
4.8
0.03 0.46 1.73 19.20 12.50 2.47 - 550
(80)
41 - For low carbon of 18% Cr-8% Ni - 2.5% Mo stainless steel.
ER-316Lsi 0.022 0.85 1.80 19.25 12.6 2.45 - 550
(80)
41 - For low carbon of 18% Cr-8% Ni - 2.5% Mo stainless steel with higher silicon content
ER-317/
ER-317L
  0.02 0.40 1.72 19.10 13.54 Mo
3.50
410
(59)
570
(83)
39 - For welding similar stainless steels.Offers higher resistance to pitting and crevice corrosion.
ER-318   0.045 0.52 1.86 18.95 11.75 2.45 Use for welding of Base Metal Grade of 316Ti
ER-320   0.02 0.27 0.46 19.73 33.48 Mo
2.12
cb&Ta
0.40
Cu3.20
460
(67)
610
(88)
41 - For welding similar metals in wrought and cast forms. good corrosion resistance to a wide range of chemical environments.
ER-347
ER-347L
  0.03 0.41 1.68 20.22 9.87 Cb&Ta
0.88
450
(65)
616
(89)
39 - For welding 321 and 347. Niobium stabilized reduce chance of chromium carbide precipitation and consequent intergranular corrosion.
ER-410   0.06 0.41 0.53 12.93 0.42 Mo 850oC*2 hr. - For welding types 403, 410, and 416. Also used as overlay on carbon steels to resist corrosion, erosion or acbrasion.
310
(45)
530
(77)
35
ER-410
NiMo
  0.03 0.41 0.54 12.15 4.12 Mo
0.62
850oC*2 hr. as weld HRC
37-40
For welding cast and wrought material of similar chemical composition.
850
(123)
950
(138)
17
ER-430   0.06 0.38 0.55 16.79 0.45 Mo
0.16
850oC*2 hr.
   
- For welding similar alloys, overlay and thermal spraying. Good ductility in head-treated condition.
ER-383   0.02 0.22 2.63 29.2 36.4 Mo
4.35
Nb
1.83
350
(51)
550
(80)
30 - For welding 825,alloy 28 and alloy 20.Corrosion resistance characteristics.
ER-385   0.02 0.35 1.71 20.2 25.60 Mo
4.52
Cu 1.5
410
(59)
610
(88)
35 -196o,
130
(-321o,
96)
For welding similar metals and for fabrication of equipment handling sulfuric acid and chloride containing media.
ER-312   0.12 0.50 1.48 29.85 9.05 - 620
(90)
770
(112)
27 - For welding dissimilar steels, high strength and high yield steels.